Hey everybody, welcome back to the lab.

Today we're going to do episode two on welding discontinuities.

Number one on the list is incomplete joint penetration.

Some of you are all too familiar with that.

You know who you are.

Number two is weld spatter.

That's spatter, not splatter.

Splatter is something you do after a night of binge drinking draft beer and eating taco bell at four in the morning.

And number three is excessive reinforcement.

Honestly, I've got nothing.

Okay, so what we've done here is we beveled the plates improperly intentionally.

So as you can see, we have a 22 .5 degree, whereas I should have a 37 .5 degree plus

or minus bevel angle for the plate if I was going to perform open root.

And then we have a root face on here.

Now typically when I do this, I would run 37 .5 degree on both plates.

I would run 332 to 8 inch root opening, and then about a 16th of an inch land.

So the land on this one's a bit excessive.

It's roughly about 332 seconds of an inch.

We have a 332nd root opening and then the 22 and a half degree bevel.

So we got a mixed up pup right here.

So hopefully we'll be able to get some incomplete joint penetration and show this to you guys.

And I kind of want to stress this just for the simple fact that as a welder, you probably spend about 80 % of your time,

your labor and prep work.

The other 20 % is going to be welding.

Okay.

That's the most technical, but how do you expect to make chicken soup from chicken right you have to start off

and set yourself up for success by doing the appropriate preparation okay

so we're going to go ahead

and tack this up i have a piece of 332nd tig rod

i'm just going to bend this into a little horseshoe

and stick that in there

and that's going to help me keep my plate spacing right where i want

it i'm going to start with this right side first get

that tacked in and then we're going to verify the gap prior to welding the other side so

So if I weld on one side, it's going to open up on the other.

So I'll just tap this back together, re -verify it with the TIG filler wire before I tack that up.

Now we're going to go ahead and throw this up in the stand.

We'll go ahead and do some vertical.

It's Friday.

Why not?

Okay, so first I'm going to light up on the tack down here.

And I'm going to get that burnt in.

And then I'm just going to start a little bit of whip and pause.

Just advancing ahead and dropping back down.

Now you'll notice I don't have as much punch as I should.

And that's mostly because of the improper bevel angle and the excessive amount of land that I have on here.

Typically, I would run a smaller land and a wider bevel.

So you can see how the filler metal is kind of bunching up in the center of that joint.

I'm probably not getting good penetration of the backside, although I can hear some faint penetration on the back.

And we'll go ahead and terminate.

Now, again, what we should do for the restart is feather this tack out, clean this joint out.

but we're kind of trying to show you exactly what not to do

and what happens if you don't do it correctly

so we're gonna go ahead and skip feathering that out just know

that you know if you do go to do a restart on open root

or any anything for that nature you should go ahead

and feather that tack back out

so you can burn back into the back side of the plate

but we're gonna be lazy today because we want to show you discontinuities

and what's causing them so we'll go ahead and tie into this

and we're just gonna keep our way

or keep working our way up the joint trying to penetrate into the back side all right

it's perfect we've got quite a few areas where i have incomplete joint penetration

that's exactly what we're trying to replicate

so as you can see in here the the weld just didn't wasn't able to punch through

that material enough and that's basically because we squeezed it together too tight

with that land now that's not to say i mean

if you ran a 3 30 second gap yeah you could penetrate through there.

Sometimes you're in the shop, you're out in the field, you know, things just aren't the way they are in a textbook.

It's not the way it's in a classroom.

You have to make adjustments.

You could turn your arc force up a little bit higher.

You could also increase your amperage.

You could put a little bit more pressure on the rod and still burn to the backside.

We're trying to show you through repetition and building good habits and things like that.

All right, so that was incomplete joint penetration.

Got another plate here.

We already put the fill one off camera

so I like to keep my fill

this one here is about just flush with the plate some spots a little bit higher than the plate

but typically what I like to do is keep my my fill pass the 16th below the weld surface

if I can do that I can almost guarantee myself

that I'll fall under that eighth inch cap

that I want to put on here

now I'm going to go just for the sake of time

I'm going to put a wider pass on here than normal you can technically qualify

that as a weave but I'm not going to,

I'm just going to bounce from side to side and kind of take my time in the middle.

This is exactly what you do not want to do.

I'm trying to replicate a high crown in the middle of this weld so that we can show you excessive weld reinforcement.

So I'm going to go slow through the center of this pass.

Typically if you're doing this correctly you would hold the sides for about two seconds

and then go fast to the middle because we're working out of position.

The center of the weld is going to take care of itself due to gravity.

So you just kind of bounce back and forth from side to side.

We'll get all the way to the top.

You'll notice also that there's not a runoff tab here.

I'm expecting, or anticipating rather,

some underfill in this section and maybe a little bit of weld metal to roll back on us once we get here,

100

once we get closer to the top because there's nothing to support that weld.

101

So what we are looking at right now is excessive weld reinforcement.

102

So ultimately I wanted to be over an eighth of an inch and it looks like we're we're right there

103

I'm about 5 30 seconds to 3 16ths in some areas.

104

That's excessive reinforcement I don't want to be anything higher than an eighth inch

105

That's why I like to say I like to work a little bit lower than an eighth of an inch

106

That way i've got a little bit of a buffer in there.

107

That is your excessive weld reinforcement

108

You want to avoid that whether it is on the roof

109

or whether it is on the surface or the cap of your plate

110

Either way, you don't want to be above an eighth of an inch

111

Once we get over 3 -8th plate, we start getting into like thicker material, one inch and above.

112

There are different criteria.

113

You are allowed to have different sizes of weld reinforcement.

114

But more or less for D11 structural stuff, it's all going to be 3 -8th plate,

115

1 -8th inch weld reinforcement on the cap or on the root.

116

So, you know, always try to keep it under 1 -8th of an inch.

117

All right, so next we have spatter, okay.

118

Spatter's pretty common.

119

A couple different ways you can get spatter, especially with the shielded metal arc welding, is the amperage.

120

If it's set way too high for the electrode, if you exceed that current carrying capacity of that electrode,

121

you're going to end up with a weld spatter.

122

Additionally, too long of an arc length.

123

If you're keeping excessive arc length, you're going to end up and get spattered that way as well.

124

Traveling too slow can also cause excessive spatter on here, spatter in general.

125

You want to try to minimize spatter.

126

It doesn't look good.

127

You can get called out for having a buckshot as it's

128

more commonly referred to on the field on your on your weld piece you may be asked to grind all that

129

that stuff off you know it's just

130

it's not a good discontinuity to have on your material you want to try to alleviate

131

that as much as possible

132

so as far as arc length you know you want to you want to keep the same diameter

133

or same arc length as the diameter of the electrode you're using

134

so for instance i was using an eighth inch electrode

135

i should maintain about an eighth inch of an arc gap for that electrode if I jump up to a 532nd.

136

Same thing, I want to maintain a 532nd arc gap in there.

137

Try to stay within the correct amperage range, go down nice slow steady travel speed, not too slow.

138

You'll notice if you start getting too slow you're going to develop spatter.

139

It's a good indication to speed up and then keep that arc length nice and consistent.

140

You're also going to get spattered all over your material, your work table it's just more for you to clean up you know

141

so try to pay attention to it if it's

142

if you're developing spatter you know maybe stop check your adjustments check your polarity settings make sure

143

you're not traveling too slow for what's going on

144

and I mean that's pretty much it spatters relatively simple to get rid of

145

so I don't want to spend too much time on

146

that one we definitely appreciate the support and until next time make everyone better than your last

147

Remember baby buggy bumpers?

148

Hey guys welcome back to the shop.

149

Yes!

150

You said welcome back to the shop.

151

Ladies and gentlemen welcome back to the shop.

152

Arc strike.

153

Arc strike.

154

Scarelessness.

155

Camera guy didn't have any fun making this video.

156

I had some fun.

157

We got to reference Pootie Tang.

158

That was fun.

159

Wadda ta sabote.

Télécharger l'application

Tout pour parler couramment

Prononciation IAChaque phrase notée

Phonétique (IPA)Maîtrisez chaque son

VocabulaireEnrichissez votre lexique

Jeu de vocabulaireApprenez en jouant

Scanner le QR

Download on theApp Store Get it onGoogle Play

Même chaîne

WELDING DEFECTS!! Porosity, Arc Strikes, Undercut

Daily ConversationUniversity StudentsWorking Adults

FOR YOU

Vidéo recommandée

96 phrases

Vocabulaire et conseils d’expression pour cette leçon

Cette leçon d’expression orale s’appuie sur la vidéo « WELDING DEFECTS!! Part 2 ». Les mots qui reviennent le plus souvent : weld, inch, spatter, arc, plate. Cette vidéo contient 159 phrases et 1796 mots à répéter en shadowing. La partie parlée dure 8:31. Le locuteur parle vite, environ 211 mots par minute : attendez-vous à des liaisons et à des sons réduits. 82 % des mots font partie des 3 000 mots les plus courants en anglais ; le reste mérite d’être vu avant de commencer.

Vocabulaire clé de cette vidéo

15 mots de la vidéo à retenir, avec leur prononciation et leur sens :

Mot	Prononciation	Sens
excessive adjectif	/ɪkˈsɛsɪv/	excessif
eighth adjectif	/eɪtθ/	huitième, huit
penetration nom	/pɛ.nəˈtɹeɪ.ʃən/	pénétration
incomplete adjectif	/ɪn.kəmˈpliːt/	incomplet
feather nom	/ˈfɛðə/	plume
angle nom	/ˈæŋ.ɡəl/	angle
punch nom	/pʌnt͡ʃ/	coup de poing
correctly adverbe	/kəˈɹɛk(t).li/	correctement
diameter nom	/daɪˈæmɪdɚ/	diamètre
bounce verbe	/baʊns/	rebondir
adjustment nom	/əˈd͡ʒʌst.mənt/	ajustement, arèglement
verify verbe	/ˈvɛɹɪfaɪ/	vérifier
restart verbe	/ˈɹiːˌstɑɹt/	recommencer
penetrate verbe	/ˈpɛnɪtɹeɪt/	pénétrer
replicate verbe	/ˈɹɛplɪkeɪt/	répliquer

Les verbes à particule que vous entendrez

Mot	Prononciation	Sens
go ahead verbe	/ˌɡoʊ əˈhɛd/	vas-y, allez-y
clean up verbe		nettoyer
end up verbe		se terminer, se finir
get over verbe		surmonter
go down verbe		descendre
speed up verbe	/spiːdˈʌp/	accélérer

Prononciation à surveiller

Le locuteur utilise 65 contractions et formes réduites, comme I'm, we're, you're. Prononcez-les sous leur forme courte, telles que vous les entendez.

Les sons « th »: eighth /eɪtθ/, feather /ˈfɛðə/, thick /θɪk/
Les sons « sh » et « zh »: penetration /pɛ.nəˈtɹeɪ.ʃən/, preparation /ˌpɹɛpəˈɹeɪʃ(ə)n/, shield /ˈʃild/, structural /ˈstɹʌk(t͡)ʃəɹəl/, indication /ɪndɪˈkeɪʃən/
Mots longs — placez bien l’accent: penetration /pɛ.nəˈtɹeɪ.ʃən/, diameter /daɪˈæmɪdɚ/, preparation /ˌpɹɛpəˈɹeɪʃ(ə)n/, technically /ˈtɛk.nɪˌkəl.i/, indication /ɪndɪˈkeɪʃən/

Les sons difficiles pour les francophones :

/h/ — il se souffle, il n’est pas muet: whereas /(h)wɛɹˈæz/, habit /ˈhæb.ɪt/, horseshoe /ˈhɔːɹs.ʃuː/
/tʃ/ et /dʒ/ — à ne pas adoucir en « ch » et « j »: punch /pʌnt͡ʃ/, adjustment /əˈd͡ʒʌst.mənt/, gentleman /ˈd͡ʒɛn.təl.mən/, binge /bɪnd͡ʒ/, amperage /ˈæm.pəɹ.əd͡ʒ/
/r/ anglais — langue recourbée, sans frotter la gorge: penetration /pɛ.nəˈtɹeɪ.ʃən/, correctly /kəˈɹɛk(t).li/, verify /ˈvɛɹɪfaɪ/, restart /ˈɹiːˌstɑɹt/, penetrate /ˈpɛnɪtɹeɪt/

Comment s’entraîner avec cette vidéo

Écoutez la vidéo en entier une fois sans parler et notez les mots que vous ne connaissez pas.
Commencez à la vitesse 0,75×, répétez phrase par phrase, puis revenez à la vitesse normale quand cela devient facile.
Enregistrez-vous et comparez avec l’original, en faisant attention à des mots comme excessive, eighth, penetration.

Qu'est-ce que la technique du Shadowing ?

Le Shadowing est une technique d'apprentissage des langues fondée sur la science, développée à l'origine pour la formation des interprètes professionnels. Le principe est simple mais puissant : vous écoutez de l'anglais natif et le répétez immédiatement à voix haute — comme une ombre suivant le locuteur avec un décalage de 1 à 2 secondes. Les recherches montrent une amélioration significative de la précision de la prononciation, de l'intonation, du rythme, des liaisons, de la compréhension orale et de la fluidité.

Technique du shadowing : lire le guide complet étape par étape →

Pratique du Shadowing: WELDING DEFECTS!! Part 2 - Apprendre l'anglais à l'oral avec la vidéo

Choisissez un mode d'entraînement

Télécharger l'application

WELDING DEFECTS!! Porosity, Arc Strikes, Undercut

Top 10 Welding Defects in Process Piping (Causes, NDT Inspection & Fixes)

Basics of Comic Shading

GC FID Operational Tutorial

Surgical Anatomy 2 (Spleen)

How Shear Deflection Impacts Deep and Composite Beams.

PCB 101 Academy - Learn how printed circuit boards are assembled

We've got separation of concerns wrong

An Animated Introduction to Vibration Analysis by Mobius Institute

Python3 For Pentesting - Introduction

Architectural Design Process Explained

Petroleum - 06 - Drilling Fluid Laboratory

The 7 Quality Control (QC) Tools Explained with an Example!